Radium Ply ISI marked Flush Doors have excellent properties in durability and dimensional stability. Various reputed buildings throughout the country have these doors that is an evidence of the commitment from RP family. Face veneers & crossbands are made from selected wood uniformly dried to optimum moisture. Kiln seasoned stiles and rails are preservative treated to improve its natural durability. Superior grade phenol formaldehyde resin manufactured resin plant provides 100% boiling water resistant bonding. Doors are pressed at high temperature and pressure, which makes them exceptionally durable and dimensionally stable.
Like all our products, each flush door is finished to perfection to provide long lasting, dependable performance. Regular tests are carried out as per IS:2202 for confirming the quality.
Radium Ply Conforms To IS:303
| TECHNICAL SPECIFICATION (IS:1659) | |||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Test | Requirement of IS 2202 | Test Result | |||||||||
| 1 | Dimensions & Squareness | Length-Width: +/5 mm Thickness: +/-1 mm Squareness: 1mm at a length of 500mm |
Length-Width: +/5 mm Thickness: +/-1 mm/-0.2 mm Squareness: 1mm at a length of 500mm |
||||||||
| 2 | General Flatness | < 6.0 mm | < 4.0 mm | ||||||||
| 3 | Local Planeness | < 0.5 mm | < 0.3 mm | ||||||||
| 4 | Impact Indentation | < 0.2 mm | < 0.2 mm | ||||||||
| 5 | Edge Loading Test | Max Deflection - < 5.0 mm Residual Deflection - < 0.5 mm Lateral Bucking -< 2.0 mm |
Max Deflection - < 3.0 mm Residual Deflection - < 0.3 mm Lateral Bucking - < 1.0 mm |
||||||||
| 6 | Shock Resistance Test | Should with stand 5 impacts | Can with stand 15 impacts | ||||||||
| 7 | Misuse Test | Pass | Excellent | ||||||||
| 8 | End Immersion Test | No delamination in one cycle | can undergo three cycles without any delamination | ||||||||
| 9 | Knife/Glue Adhesion - Test | Pass | Excellent | ||||||||
| 10 | Screw Withdrawal Resistance | > 1000 N | > 1500 N | ||||||||